Product Information
Product Name | MoSi2 Heating Elements |
Brand | YTTORCH |
Place Of Origin | CHINA |
Model No | TC1850 |
Shape | L Shape |
Size | Customizable |
Heating Element temperature (Air Environment) | 1850℃ |
Features | High compactnessand purity; The temperature resistance degree improves and it canbearlarge surface load |
Application Range | Dental materials (MgO, Y₂O₃and ZrO₃) sintering |
Product Standard specifications | |||||||||
Diameter(mm) φd(hot zone)/ φC(cold zone) |
shape |
length(mm) Le(hotzone)/ Lu(cold zone) | a(mm) | g(mm) | f(mm) | h(mm) | n(mm) | ||
Standard |
Minimum |
Standard |
Minimum | ||||||
3/6 |
U,L ,W or customized |
customized | 25 | 12 | 15 | 30 | 10 | 40 | 35 |
4/9 |
U,L ,W or customized |
customized | 25 | 15 | 20 | 30 | 10 | 50 | 45 |
6/12 |
U,L ,W or customized |
customized | 50 | 25 | 25 | 45 | 15 | 90 | 70 |
9/18 |
U,L ,W or customized |
customized |
60 | 35 | 32 | 75 | 20 | 135 | 110 |
12/24 |
U,L ,W or customized |
customized |
80 | 50 | 40 | 100 | 35 | / | / |
Product Type | Density-g/cm3 | Bending strength under room temperature-MPa | Hardness-GPa | Compression Strength-MPa | Water Absorption-% | Thermal elongation-% |
TC 1850 | 6.6±0.1 | 460 | 11 | >1500 | ≤0.2% | 4 |
Atmosphere | 1700Type | 1800Type | 1850Type | 1900Type |
Air | 1700 | 1800 | 1830 | 1850 |
Nitrogen | 1600 | 1700 | 1700 | 1700 |
Ar Ne Argon, Helium | 1600 | 1700 | 1700 | 1700 |
Dry Hydrogen (dew point)-80℃ | 1150 | 1150 | 1150 | 1150 |
Wet Hydrogen (dew point)-20℃ | 1450 | 1450 | 1450 | 1450 |
Exogas(e.g. 10% CO2, 50% CO, 15%H2) | 1600 | 1700 | 1700 | 1700 |
Exogas(e.g. 40% CO2, 20% CO) | 1400 | 1450 | 1450 | 1450 |
Cracked and partially burnt ammonia(8%H2) | 1400 | 1450 | 1450 | 1450 |